Multilayer hard coating for tools

ABSTRACT

A multilayer hard coating for tools for machining applications with a multilayer structure for improving the wear resistance of workpieces includes at least one (Al y Cr 1-y ) X layer (0.2≦y≦0.7), wherein X is one of the following elements N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, CBNO, but preferably N or CN, and/or a (Ti z Si 1-z ) layer (0.1≦z≦0.3). The hard coating also includes at least one layer stack with one (AlCrTiSi) X mixed layer, followed by another (Ti z Si 1-z ) X layer, followed by another (AlCrTiSi) X mixed layer, followed by another (Al y Cr 1-y ) X layer.

TECHNICAL FIELD

This invention concerns a multilayer hard coating for tools (hard metal and high-speed steel) for machining applications—especially drilling applications.

-   -   1a) Tools coated with hard coatings, with a series of several         different aluminum chromium nitride or carbonitride and titanium         silicide nitride or carbonitride layers     -   1b) Tools, especially cutting and forming tools (drills,         millers, taps, formers, roller cutters, stamps, dies, drawing         stamps, etc.) with a series of several different aluminum         chromium nitride or carbonitride and titanium silicon nitride or         carbonitride layers and the use of such tools     -   1c) A method of producing a series of several different aluminum         chromium nitride or carbonitride and titanium silicon nitride or         carbonitride layers with a defined layer structure.

STATE OF THE ART

EP 1174528 A2 describes a tool coating comprised of a series of several individual layers, wherein the first layer is composed of a nitride, carbide, carbonitride, boride, oxide, etc. of the elements Ti, Al and/or Cr, and a second layer is composed of a nitride, carbide, carbonitride, boride, oxide etc. of Si and at least one element from groups 4a, 5a and 6a of the PTE [Periodic Table of the Elements]. The advantage of this coating is that the Si in the upper layer critically improves the wear resistance and oxidation resistance. The Cr—Si-based cover layers mainly improved tool life. TIAIN, CrAIN and TiN layers are chosen for the bottom layer.

EP 1422311 A2 describes Al—Cr—(Si)—O-based hard layers that can be made as nitrides, carbide, oxide, boride, etc. For all layers, it is true that a small percentage of oxygen (1-25%) is contained in the layers. It should also be mentioned that another hard layer can be applied in the coating mentioned in the invention. Ti—Si—N Ti—B—N, BN, Cr—Si—N, etc., inter alia, are given here as examples. One advantage of the invention is the use of small quantities of oxygen or silicon and oxygen, since this results in greater hardness, improved wear resistance and high-temperature oxidation resistance.

EP 1219723 A2 introduces a Ti—Al—Cr—X—N-based coating, where X can stand for Si, B and/or C. The advantage of this coating is to improve wear-resistance compared to conventional coatings. The invention also describes a target that must be composed of at least Ti, Al and Cr.

DISADVANTAGES OF THE STATE OF THE ART

The tools with hard coatings in the state of the art (Ti—Al—N-based coatings) have shorter tool lives than the new optimized (Al_(1-x)Cr_(x)X)—Ti_(1-y)Si_(y)) X-hard coatings for X═N or CN.

The disadvantages of the state of the art are also that with Al—Cr—N coatings at high temperatures in an atmosphere of inert gas (for example, an argon atmosphere), the coating starts to decompose at around 900° C. If this heat-treatment process is carried out in an atmosphere of oxygen, the decomposition process goes into a higher temperature range. Now, if a continual cut is being considered in machining, the local temperatures are very high (sometimes over 1000° C.) in the contact area between the surface of the tool and the workpiece. If this contact surface is large enough so that no/little oxygen can have a stabilizing effect on the coating surface, the cubic CrN breaks down into hexagonal Cr₂N and then at a higher temperature into metallic Cr. This coating decomposition process results in premature wear on the coating in use, which manifests as crater wear in particular.

PROBLEM OF THE INVENTION

The purpose of the invention is to prevent the disadvantages of the state of the art and especially to improve the tool life of coated tools, like chip removal tools, for example, cutting and forming tools and components for machinery and forming. It is also the problem of the invention to provide a method of cutting such coatings, especially cutting such coatings on sawn workpieces.

SOLUTION OR PATH TO SOLUTION

The invention solves this problem with the hard coating in claim 1 and the tool with such a coating in claim 12. Other inventive embodiments are described in the subclaims.

The invention describes a special multi-layer design for a coating to prevent the coating from disintegrating too fast (wearing out) during use. The multi-layer design prevents or at least delays the disintegration and subsequent diffusion of the Cr—N portion in the AlCrN coating at high temperatures.

An RCS-type industrial coating system from the Balzer Company is used for the deposition of the Al—Cr—(X)—N/Ti—Si—N hard layers, as described, for example, in EP 1186681 in FIGS. 3 to 6 and the Description, column 7, line 18 to column 9, line 25. For this, the cleaned workpieces, depending on their diameter, attached to two or, for diameters smaller than 50 mm, to three rotating substrate holders and two Ti—Si targets produced by fusion metallurgy and four targets made of Al—Cr—(X) alloys produced by powder metallurgy are installed in six cathode arc sources placed on the walls of the coating system. The geometry of the target layout is basically determined by the octagonal plot of the RCS system, in which two heating segments arranged opposite each other separate two groups of three segments in a row with an arc cathode. For these experiments, an SiTi target was installed in the opposite middle element of each group of three. But other target layouts are also possible to produce such layers. In principle, such layers can be deposited in each system that has at least two arc cathodes in a geometrically equivalent position, for example at the same coating height of one or more rotating substrate holders. An expert knows it is possible to further influence the thickness of the individual layers or laminates by arranging the target or setting the respective substrate movement or rotation or the angular speed of rotation of a workpiece, depending on the type of system.

Next, the workpieces are brought to a temperature of approximately 500° C. by radiational heating also placed in the system and then the surface undergoes etch cleaning by Ar ions by applying a DC bias voltage of −100 to −200 V in an Ar atmosphere at a pressure of 0.2 Pa.

After that, an Al—Cr—N adhesive layer approximately 0.2 μm thick is deposited by operating four Al—Cr sources with a capacity of 3′ kW and applying a substrate bias of −50 V for a period of approximately 5 minutes. Then, a multilayer coating is purposely created, in which first 2 Ti-Si sources also with 3 kW are connected to the 4 Al—Cr sources, and they are operated together for a period of approximately 1 minute. Then the 4 Al—Cr sources are turned off and a pure Ti—Si—N coating is deposited for approximately 3 meetings. Then the 4 Al—Cr sources are connected to it again for approximately 1 minute. After that, the TiSi sources are turned off, and a pure Al—Cr—N coating is deposited for another 5 minutes. This sequence for the layer stack is followed several times during the deposition in the invention. Finally, another cover layer approximately 0.5 μm thick is applied, which was produced exclusively with the Ti—Si sources. Alternately, a thicker AlCrN cover layer can be applied here. All layers were deposited in an atmosphere of pure nitrogen at a pressure of around 3 pa and a negative substrate preliminary voltage of roughly 50 volts. Basically the process pressure in each of these steps can be set in a range from 0.5 to around 8 pa, but preferably between 0.8 and 5 Pa, whereby the atmosphere can be either pure nitrogen or a mixture of nitrogen and an inert gas, like argon, for nitride layers, or a mixture of nitrogen and a gas containing carbon, which can be mixed with an inert gas if necessary can be used for carbonitride layers. Accordingly, oxygen or a gas containing boron can be mixed in, as is known, for the deposition of layers containing oxygen or boron.

Table 1 shows the composition of the target, the crystal structure of the layer and the adhesion. Table 2 summarizes the process parameters, such as the target capacity, negative substrate preliminary voltage, process pressure and temperature.

According to the invention, workpieces are distinguished by the fact that a cubic (Al_(y)Cr_(1-y)) X layer is deposited with X═N or CN, but preferably N, and 0.2≦y≦0.7, preferably 0.3≦y≦0.5 alternating with a cubic (TizSi_(1-z)) X layer with X═N or CN, but preferably N, and 0.99≦z≦0.7, preferably 0.97≦z≦0.85 (see FIG. 1 a), whereby at least one layer stack and at least one additional (Al_(y)Cr_(1-y))X or (Ti_(z)Si_(1-z))X layer is applied. The structure of the layers is microcrystalline in both layers with an average grain size of approx. 5-150 nm, but preferably from approximately 10-120 nm.

One advantage of the coating is the additional intermediate layers between the pure (Al_(y)Cr_(1-y)) X and (Ti_(z)Si_(1-z)) X layers, in which all coating sources run and thus an (Al_(y)Cr_(1-y)Ti_(z)Si_(1-z)) X layer is deposited (see FIG. 1 b). These intermediate layers can, if necessary, depending on the sequence or composition and properties of the individual layer systems, bring about improved adhesion between the individual layers. Due to the geometric target arrangement within the coating system, because of the rotation of the workpiece during the deposition of this intermediate layer, a multilayer structure with very fine layers is also deposited, since as before individual Al—Cr-based and Ti—Si-based targets are used for the coating. The width of the individual layers within this intermediate layer is in the range of several nanometers.

Another way of designing the desired multilayer system, can be by periodically turning the coating sources on and off similarly to FIG. 1 c. Here, the coating sources for a coating material run during the whole deposition process, while the coating sources with the second coating material are switched on periodically. In this case, an additional multilayer structure, as mentioned above, can be produced while the arc sources operate together.

The method in the invention is characterized by the fact that a process is chosen in order to deposit the layer stack described above. The multilayer structure is achieved by purposely turning the coating sources on and off. The multilayer substructure is maintained in addition by rotating or moving the workpieces being coated within the coating system.

Example 1 describes coatings with a defined number of layers or packets of layers, whereby a layer stack consists of a sequence of AlCrTiSiN layers followed by a layer of TiSiN, AlCrTiSiN and AlCrN. It is easy to see that compared to the layer tested in Experiment No. 1, which was deposited according to the state of the art, an improvement in tool life can be achieved with the coating in the invention. It is also clear that the optimal layer thickness of the individual layers made of Al_(y)Cr_(1-y)N and Ti_(z)Si_(1-z)N is important for the necessary increase in tool life. This layer thickness for Al_(y)Cr_(1-y)N is between 75 nm and 200 nm, preferably 120 nm to 170 nm, and for Ti_(z)Si_(1-z)N between 50 and 150 nm, preferably between 70 to 120 nm. In this example, these layer thicknesses were altered over the coating time so that for all experiments, a comparable layer thickness of roughly 4 μm could be achieved. For these experiments, a layer design was chosen like the one described in FIG. 1 b. The layers, in which all coating sources were used, were not changed for the respective experiments and yielded an individual layer thickness of around 20±10 nm, respectively.

Basically, completely different workpieces can be coated advantageously with these kinds of Al_(y)Cr_(1-y)N/Ti_(z)Si_(1-z)N multilayer coatings. Examples of this are cutting tools like milling cutters, hob cutters, spherical head cutters, planar and profile cutters and drills, taps, shaving dies, reamers and indexable inserts for lathe and mill work and forming tools like stamps, dies, drawing dies, knockout cores or thread formers. Also injection-molding tools, for example for metal injection-molding alloys, synthetic resins or thermoplastics, especially injection-molding tools like those used for producing plastic molded parts or data carriers like CDs, DVDs et al., can be protected advantageously with such layers. Although better results are not always achieved by the coatings in the inventions for all applications on different tools, much higher wear resistance can be achieved, at least on certain applications and in the examples listed than with the coatings known in the past.

In addition, because of the behavior of Al_(y)Cr_(1-y)N/Ti_(z)Si_(1-z)X multilayer coatings, which is similar in principle, an improvement in wear behavior can be expected when target compositions and coating parameters in the following layer systems are chosen so that X═N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO and CBNO, but preferably N and CN and 0.2≦y≦0.7, preferably 0.40≦y≦0.68 and 0.01≦z ≦0.3, preferably 0.05≦z≦0.15.

One way of improving the coating properties of Al_(y)Cr_(1-y)N/Ti_(z)Si_(1-z)N multilayer coatings consists of alloying other chemical elements from one or more groups of Groups IVb, Vb and/or VIb of the Periodic Table of the Elements, or silicon. It can be especially advantageous to alloy with the layer stack of the Al_(y)Cr_(1-y)−M_(m)N layer, with 0≦m≦0.25, preferably with 0≦m≦0.15. The elements for M=W, V, Mo, Nb and Si have proven particularly advantageous (see Example No. 5).

Another way of improving the properties of the layer system is to put an extra sliding layer on the layer stack or on the cover layer closing the hard coating on the outside. The sliding coating system can be made of at least one metal or a carbide of at least one metal and disperse carbon, MeC/C, whereby the metal is a metal from the Group IVb, Vb and/or VIb and/or silicon. For example, a WC/C cover layer with a hardness that can be set between 1000 and 1500 HV that has excellent intake properties is especially suitable for this. CrC/C coatings also have similar behavior with a somewhat higher friction coefficient.

With such coated deep-hole drills, after a bore hole was produced, it was possible to detect additional intake smoothness of the chip surfaces, which has only be achieved to date by expensive mechanical machining. This results in an improvement in chip transport along the chip groove and minimization of friction torque during the drilling process. Such properties are also of interest particularly for component applications with sliding, rubbing or rolling stresses, especially when there is a lack of lubrication or when they run dry, or if an uncoated counter body must be protected at the same time.

Other ways of making a sealing sliding coating are metal-free diamond-like carbon coatings, or MoS_(x), WS_(x) or MoS_(x) or MoW_(x) layers containing titanium.

The sliding layer can be applied, as mentioned, directly to the multilayer system or after another adhesive layer is applied, in order to achieve the best possible adhesion of the layer composite. The adhesive layer can be designed to be made of metal, nitride, carbide, carbonitride or as a gradient layer.

For example, WC/C or CrC/C layers can be produced, after applying a sputtered or arced Cr or Ti adhesive layer, advantageously by sputtering a WC target while adding a gas containing carbon. Here, the percentage of gas containing carbon is increased over time to achieve a larger percentage of free carbon in the layer.

OTHER ADVANTAGEOUS EFFECTS OF THE INVENTION

The following will show advantageous applications of the invention, as examples, using different cutting operations.

EXAMPLE 1

Drills with inner-cooled HM drill bits of structural steel

-   Tool: Hard metal drill with cooling ducts     -   Diameter D=6.8 mm -   Workpiece: Structural steel DIN 1.1191 (Ck45) -   Drilling parameters: Cutting speed v_(c)=120 m/min     -   Tooth feed f_(z)=0.2 mm/rotation     -   Hole depth z=34 mm (5xD) -   Cooling: 5% emulsion -   Process: blind hole

Wear criterion: Corner wear VB=0.2 mm Tool life expressed in units Layer of length of path thickness traversed** Experiment No. [μm] [m] 1 AlCrN + TiSiN 3.9 54.3 2 AlCrN + 2 × layer stack 1* + TiSiN 4.2 43.9 3 AlCrN + 4 × layer stack 1* + TiSiN 3.9 65.2 4 AlCrN + 8 × layer stack 1* + TiSiN 4.0 76.2 5 AlCrN + 12 × layer stack 1* + TiSiN 4.0 54.3 6 AlCrN + 15 × layer stack 1* + TiSiN 3.9 43.9 *A (1×) coating stack corresponds to a one-time sequence of “AlCrTiSiN + TiSiN + AlCrTiSiN + AlCrN.” **In which the width of the wear land was VB = 0.2 mm.

Example 1 shows a comparison of the tool lives of coated HM drills, in which a different number of coating stacks were applied with the same adhesive layer, namely AlCrN and a cover layer, namely TiSiN. The coating time of the TiSiN and AlCrN layers was adjusted so that in the end, the total thicknesses of the layers were comparable. An optimum total tool life was found in Experiment No. 4 with a total number of 37 layers, which shows a clear improvement over the state of the art from Experiment No. 1.

EXAMPLE 2

Drills with inner-cooled HM drills of structural steel

-   Tool: Hard metal drill with cooling ducts     -   Diameter D=6.8 mm -   Workpiece: Structural steel DIN 1.1191 (Ck45) -   Drilling parameters: Cutting speed v_(c)=120 m/min.     -   Tooth feed f_(z)=0.2 mm/rotation     -   Hole depth z=34 mm (5xD) -   Cooling: 5% emulsion -   Process: Blind hole

Wear criterion: Corner wear VB=0.2 mm Tool life expressed in length of path traversed Experiment No. with VB = 0.2 mm in meters  6 (TiAlN/TiN multilayer) 32.3  8 (TiAlN monolayer) 32.3  9 (AlCrN monolayer) 65.9 10 AlCrN + 8 × layer stack 1* + TiSiN 76.2

Example 2 shows a comparison of the tool lives of coated HM drill bits. Here, an improvement in tool life was also able to be achieved with the AlCrN/TiSiN multilayer compared to hard coatings of TiAIN/TiN multilayer and TIAIN monolayer coatings used industrially.

EXAMPLE 3

Drills with outer-cooled HM drill bits of structural steel

-   Tool: Hard metal drill with cooling ducts     -   Diameter D=6.8 mm -   Workpiece: Structural steel DIN 1.1191 (Ck45) -   Drilling parameters: Cutting speed v_(c)=120 m/min.     -   Tooth feed f_(z)=0.2 mm/rotation     -   Hole depth z=23.8 mm (3.5xD) -   Cooling: 5% emulsion -   Process: Blind hole

Wear criterion: Corner wear VB=0.15 mm Tool life expressed in length of path traversed Experiment No. with VB = 0.15 mm in meters 11 (TiAlN/TiN multilayer) 46.1 12 (TiAlN monolayer) 42.3 13 (AlCrN monolayer) 22.6 14 AlCrN + 8 × layer stack 1* + TiSiN 61.5

Example 3 shows a comparison of the tool lives of coated HM drill bits. Here, an improvement in tool life was also able to be achieved with the AlCrN/TiSiN multilayer compared to hard TiAIN-based coatings used industrially.

EXAMPLE 4

Drills with inner-cooled HM drill bits of cast iron (GGG-50)

-   Tool: Hard metal drill with cooling ducts     -   Diameter D=6.8 mm -   Workpiece: Cast iron with spherical graphite GGG50 -   Drilling parameters: Cutting speed v_(c)=200 m/min.     -   Tooth feed f_(z)=0.3 mm/rotation     -   Hole depth z=34 mm (5xD) -   Cooling: 5% emulsion -   Process: Blind hole

Wear criterion: Corner wear VB=0.1 mm Tool life expressed in length of path traversed Experiment No. with VB = 0.1 mm in meters 15 (TiAlN/TiN multilayer) 57.1 16 (TiAlN monolayer) 142.8 17 (AlCrN monolayer) 185.6 18 AlCrN + 8 × layer stack 1* + TiSiN 199.9

Example 4 shows a comparison of the tool lives of coated HM drill bits. Here, an improvement in tool life was also able to be achieved with the AlCrN/TiSiN multilayer coating compared to hard layers of TiAIN/TiN multilayer coating and TIAIN monolayer coatings used industrially.

EXAMPLE 5

Drills with inner-cooled HM drill bits of structural steel

-   Tool: Hard metal drill with cooling ducts     -   Diameter D=6.8 mm -   Workpiece: Structural steel DIN 1.1191 (Ck45) -   Drilling parameters: Cutting speed v_(c)0=120 m/min.     -   Tooth feed f_(z)=0.2 mm/rotation     -   Hole depth z=34 mm (5xD) -   Cooling: 5% emulsion -   Process: Blind hole

Wear criterion: Corner wear VB=0.2 mm Tool life expressed Layer in length of path Al Cr M thickness traversed with VB = 0.2 mm Experiment No. at % at % at % [μm] in meters 19 AlCrWN + 8 × layer stack 2* + TiSiN 70 28 2 3.8 65.8 20 AlCrWN + 8 × layer stack 2* + TiSiN 70 25 5 3.4 59.3 21 AlCrNbN + 8 × layer stack 2* + TiSiN 70 25 5 3.8 57.8 22 AlCrMoN + 8 × layer stack 2* + TiSiN 70 25 5 4.8 61.2 23 AlCrVN + 8 × layer stack 2* + TiSiN 70 25 5 4.2 68.0 24 AlCrSiN + 8 × layer stack 2* + TiSiN 70 25 5 4.0 54.4 *A (1×) layer stack 2* corresponds to a one-time coating sequence of “AlCrMTiSiN + TiSiN + AlCrMTiSiN + AlCrMN,” wherein M stands for one of the elements W, Nb, Mo V or Si.

Example 5 shows a comparison of the tool lives of HM drills coated according to the invention on which multilayer systems with different chemical compositions, but the same cover layer (TiSiN) were deposited. As a chemical composition, the target composition was varied, wherein Al was kept constant, and Cr was partly replaced by a third element. The process parameters for layer deposition were kept equal as in the other experiments.

Another way of producing a corresponding layer stack is when, as in FIG. 1 c, either the AlCr or AlCrM sources or the TiSi source or sources are operated constantly and the other source or sources are turned on as needed. In particular with constant operation of the above-mentioned 4 AlCr or AlCrM sources, the deposition rate can be increased, and the following layer system can be deposited, for example:

-   -   one (AlCrTiSi) X mixed layer     -   followed by another (Al_(y)Cr_(1-y)) X layer     -   followed by another (AlCrTiSi) X mixed layer     -   followed by another (Al_(y)Cr_(1-y)) X layer.

DESCRIPTION OF FIGURES

FIG. 1 shows different layer variations. FIGS. 1 a-c discuss three variations of how a multilayer coating can be made.

FIG. 1 a shows a sequence of layers with sharp transitions. A layer system (2) is deposited directly on a second layer system (1). This process is repeated until the desired total layer thickness is reached. A cover layer (3) with higher thicknesses can be deposited as the last layer.

In FIG. 1 b, mixed layers (4) in which both layer systems are applied simultaneously are deposited between the individual layers. The mixed layer can be made either thin as a sliding transitional layer or thicker with an area where the composition of the layer is constant. Such a layer can have the following composition, for example: Al=40.7 at %, Cr=21.2 at %, Ti=32.8 at % and Si=5.3 at %. This composition comes about when AlCr targets with a composition of Al=70 at % and Cr=30 at % and TiSi targets with a composition of Ti=85 at % and Si=15 at % are used simultaneously. In general, the composition of a mixed layer with a constant composition is advantageously set in the following range: (Al _(1-a-b-c) Cr _(a) Ti _(b) Si _(c)) X where 0.18≦a≦0.48; 0.28≦b≦0.4; 0.004≦c≦0.12. The aluminum content is advantageously kept at over 10 at %. If other elements are added, as mentioned above, to achieve a corresponding effect, depending on the element, a minimum concentration of 0.5 to 1 atom percentage and a maximum concentration of 15% to 25% are added.

In FIG. 1 c, a multilayer coating is deposited by applying a layer system (5) during the whole coating time, and the second layer system is periodically mixed in with it by turning on the corresponding coating source.

FIG. 2 shows the design of the layer packet in FIG. 1 in an altered view. TABLE 1 Composition of Target Target 1 Layer Crystal Al Cr Target 2 Thickness Experiment Structure at % at % M at % Ti at % Si at % [μm] Adhesion A B1 70 30 — 85 15 4.0 HF1 B B1 70 28 W = 2 85 15 3.8 HF1 C B1 70 25 2 = 5 85 15 3.4 HF1 D B1 70 25 Nb = 5 85 15 3.8 HF1 E B1 70 25 V = 5 85 15 4.8 HF1 F B1 70 25 Mo = 5 85 15 4.2 HF1 G B1 70 25 Si = 5 85 15 4.0 HF1

TABLE 2 P_(Target)Al—Cr-M P_(Target)Ti—Si U_(Substrate) P_(N2) Temp. Experiment [kW] [kW] [V] [Pa] [° C.] A 3 3 −50 3 500 B 3 3 −50 3 500 C 3 3 −50 3 500 D 3 3 −50 3 500 E 3 3 −50 3 500 F 3 3 −50 3 500 G 3 3 −50 3 500 

1. A hard layer with a multilayer structure for improving the wear resistance of workpieces that comprising: at least one (Al_(y)Cr_(1-y)) X layer, wherein 0.2≦y≦0.7 and X is one of the following elements N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, CBNO, but preferably N or CN, and/or a (Ti_(z)Si_(1-z)) layer, wherein 0.01≦z≦0.3, characterized by the fact that the hard layer also includes at least one layer stack with the following composition: one (AlCrTiSi) X mixed layer followed by another (Ti_(z)Si_(1-z)) X layer followed by another (AlCrTiSi) X mixed layer followed by another (Al_(y)Cr_(1-y)) X layer.
 2. The hard coating in claim 1, characterized by the fact that the at least one (Al_(y)Cr_(1-y)) X layer, the other (Al_(y)Cr_(1-y)) X layer and the (AlCrTiSi) X mixed layers contain at least one other element from Group IVb, Vb and/or VIb of the Periodic Table of the Elements, or silicon.
 3. The hard coating in claim 1, characterized by the fact that the at least one (Al_(y)Cr_(1-y)) X layer, the other (Al_(y)Cr_(1-y)) X layer contain 0.5 to 25 atom % of the other element or silicon, setting the concentration of the elements and of the silicon is set in the other (AlCrTiSi) X mixed layers.
 4. The hard layer in claim 1, characterized by the fact that the layers in the layer stack have the following thickness: Al_(y)Cr_(1-y)N between 75 nm and 200 nm Ti_(z)Si_(1-z)N between 50 and 150 nm (AlCrTiSi) X mixed layers 20±10 nm.
 5. The hard layer in claim 1, characterized by the fact that the layer includes several layer stacks in a row.
 6. The hard layer in claim 5, characterized by the fact that the layer packet contains 4, 8 or 12, but preferably 8 layer stacks.
 7. The hard coating in claim 1, characterized by the fact that at least one (Al_(y)Cr_(1-y)) X layer is deposited directly on the workpiece or on an adhesive layer.
 8. The hard coating in claim 1, characterized by the fact that a (Al_(y)Cr_(1-y)) X cover layer or a (Ti_(z)Si_(1-z)) X form the outer last layer of the hard coating.
 9. The hard coating in claim 1, characterized by the fact that an additional sliding layer is deposited on the hard coating.
 10. The hard coating in claim 1, characterized by the fact that the at least one layer stack includes the following: one (AlCrTiSi) X mixed layer followed by another (Al_(y)Cr_(1-y)) X layer followed by another (AlCrTiSi) X mixed layer followed by another (Al_(y)Cr_(1-y)) X layer.
 11. The hard layer in claim 1 or 10, characterized by the fact that the mixed layers contain a multilayer structure.
 12. A workpiece, characterized by the fact that the workpiece includes the coating in claim 1 or
 10. 13. The workpiece in claim 12, characterized by the fact that the workpiece is a component for machining and forming, a tool, a machining tool, a cutting or forming tool, but preferably a drill. 